Mechanical and Wear Properties of Cold Extruded Al6063 Metal Matrix Alloy Reinforced with Silicon Carbide, Alumina and Cerium Oxide

  • 1. Research Scholar, Department of Mechanical Engineering, Ghousia college of Engineering, Visvesvaraya Technological University, Balgavi, Karnataka, India
  • 2. Professor & Principal, Islamiah Institute of Technology, Bangalore, Visvesvaraya Technological University, Balgavi, Karnataka, India
  • 1. Publisher

Description

Metal matrix composite is considered in various engineering fields like Automobile, medical, electronics aerospace, marine, recreational sectors, of which Aluminum metal matrix composite is considered mostly because of its high strength to weight ratio, easy of fabrication, corrosion resistance, good aesthetic appearance and high resistance to wear etc. This paper concentrates on the effect of secondary processing (Cold Extrusion) on mechanical and wear properties of Al6063 reinforced with SiC, Al2O3 and CeO2 particles. Here composite systems prepared by varying reinforcement from 0% to 8% in steps of 2%. Stir casting route adopted for casting composite systems after casting the composite is made to pass through extrusion process with an extrusion ratio of 1.93 with a total strain of 1.45. All composite systems tested for mechanical properties as per ASTM and ISO standard. Wear test was conducted on pin on disc setup for different loads, reinforcement, sliding distance and sliding speed. Results reveals that due increase in reinforcement the mechanical properties have improved further improvement observed when subjected to extrusion process, similar observation was made for wear studies which conclude the wear rate is improved for extruded composite as compared to cast composite systems observed by various researchers.

Files

C6219029320.pdf

Files (854.8 kB)

Name Size Download all
md5:fc434fc8584b40a46a99bc3faf9a8010
854.8 kB Preview Download

Additional details

Related works

Is cited by
Journal article: 2249-8958 (ISSN)

Subjects

ISSN
2249-8958
Retrieval Number
C6219029320/2020©BEIESP