Published November 24, 2019 | Version v1
Journal article Open

Interaction of aluminum with fluorine-containing salt melts

Creators

Description

The interaction of solid aluminum with salt melt systems of the KAlF4-KBF4-KCl system in the temperature interval (оС) 470÷600 was studied. As a result of the metallothermic reaction, a boron powder of black-brown color with particle size distribution of 0.1÷0.01 mm was obtained. An increase in the amount of interaction product with increasing temperature, content of potassium tetrafluoroborate in the melt and the specific surface of aluminum samples was noted.

Files

Природничі науки_2019_Print-79-83.pdf

Files (525.4 kB)

Additional details

References

  • Бугаєнко В. В., Мартинюк О. О. Низькоплавкі флуоровмісні розчинники оксиду алюмінію // Природничі науки: Збірник наукових праць. 2013. Вип. 10. С. 138–143.
  • Волков А. И., Жарский И. М. Большой химический справочник. Мн.: Современная школа, 2005. 608 с.
  • Малишев В. В. Високотемпературна електрохімія та електроосадження металів IV–VIА груп і їх сполук в іонних розплавах. К.: Університет «Україна», 2004. 326 с.
  • Самсонов Г. В., Серебрякова Т. Н., Неронов В. А. Бориды. М.: Атомиздат, 1975. 356 с.
  • Серебрякова Т. И., Неронов В. А., Пешев П. Д. Высокотемпературные бориды. М.: Металлургия, Челяб. отд-е, 1991. 367 с.
  • Lai J., Zhang Z., Chen X.-G. The thermal stability of mechanical properties of Al–B4C composites alloyed with Sc and Zr at elevated temperatures // Materials Science and Engineering. 2012. Vol. 532. P. 462–470.
  • Lin Y., Li Q., Fan Sh. Self-catalуtіc growth of aluminium borate nanowires // Chem. Phys. Letters. 2003. 375, № 5–6. P. 632–635.
  • Lovering D. G. Molten salt technology. New York: Plenum Press, 1982. 530 p.
  • Pat. 5531425 USA. Apparatus for continuously preparing castable metal matrix composite material / M. D. Skibo, D. M. Schuster, R. S. Bruski : Alcan Aluminum Corporation ; filing 07.02.1994 ; publ. 02.07.1996.
  • Pat. 6602314 USA. Aluminum composite material having neutron-absorbing ability / Y. Sakaguchi, T. Saida, K. Murakami, K. Shibue, N. Tokizane, T. Takahashi : Mitsubishi Heavy Industries, Ltd ; filing 27.07.2000 ; publ. 05.08.2003.
  • Wang X. The formation of AlB2 in an Al–B master alloy // J. Alloys and Compounds. 2005. 403. P. 283–287.