Enhancement of Mechanical Properties for Al-Mg-Si Alloy Using Equal Channel Angular Pressing
Creators
Description
Equal channel angular pressing (ECAP) of
commercial Al-Mg-Si alloy was conducted using two strain rates.
The ECAP processing was conducted at room temperature and at
250°C. Route A was adopted up to a total number of four passes in
the present work. Structural evolution of the aluminum alloy discs
was investigated before and after ECAP processing using optical
microscopy (OM). Following ECAP, simple compression tests and
Vicker’s hardness were performed. OM micrographs showed that, the
average grain size of the as-received Al-Mg-Si disc tends to be larger
than the size of the ECAP processed discs. Moreover, significant
difference in the grain morphologies of the as-received and processed
discs was observed. Intensity of deformation was observed via the
alignment of the Al-Mg-Si consolidated particles (grains) in the
direction of shear, which increased with increasing the number of
passes via ECAP. Increasing the number of passes up to 4 resulted in
increasing the grains aspect ratio up to ~5. It was found that the
pressing temperature has a significant influence on the
microstructure, Hv-values, and compressive strength of the processed
discs. Hardness measurements demonstrated that 1-pass resulted in
increase of Hv-value by 42% compared to that of the as-received
alloy. 4-passes of ECAP processing resulted in additional increase in
the Hv-value. A similar trend was observed for the yield and
compressive strength. Experimental data of the Hv-values
demonstrated that there is a lack of any significant dependence on the
processing strain rate.
Files
10000442.pdf
Files
(671.2 kB)
| Name | Size | Download all |
|---|---|---|
|
md5:a2de79aeaa4151beeda2812a1a4f1b44
|
671.2 kB | Preview Download |
Additional details
References
- Y. Estrin, and A. Vingoradov, Extreme Grain Refinement by Severe Plastic Deformation: A Wealth Of Challenging Science, Acta Materialia 61, 2013, pp. 782-817.
- X.Z. Liao, X.Z. Liao, Y. H. Zhao, E.J. Laverina, S.P. Ringer, Z. Horita, T.G. Langdon, and Y.T. Zhu, The Role of Stacking Faults and Twin Boundaries in Grain Refinement of A Cu–Zn Alloy Processed by High- Pressure Torsion, Materials Science and Engineering A 527, 2010, pp. 4959-4966.
- R.Z. Valiev and T.G. Langdon, Principles of Equal-Channel Angular Pressing as A Processing Tool For Grain Refinement, Prog. Mater. Sci. 51, 2006, pp. 881-981.
- R.Z. Valiev, R.K. Islamgaliev, and I.V. Alexandrov, Bulk Nanostructured Materials from Severe Plastic Deformation, Prog. Mat. Sci. 45, 2000, pp.103-189.
- S. Ji, D. Watson, Y. Wang, M. White, and Z. Fan, Effect of Ti Addition on Mechanical Properties of High Pressure Die Cast Al-Mg-Si Alloys, Materials Science Forum Vol. 765, 2013, pp 23-27.
- Y. Birol, Precipitation During Homogenization Cooling in AlMgSi alloys, Trans. Nonferrous Met. Soc. China 23,2013, pp. 1875-1881.
- Hirsch, B. Skrotzki, and G. Gottstein, Aluminium Alloys, Their Physical and Mechanical Properties, Wiley-VCH, Weinheim, Germany, 2008.
- W. Hufnagel, Key to Aluminium Alloys, Aluminium Publication, Dusseldorf, Germany, 1999.
- G. Dieter, Mechanical Metallurgy, SI Metric Edition, McGraw-Hill, London, UK, 1988. [10] J.K. Kim, H.K. Kim, J.W. Park and W.J. Kim, Large enhancement in mechanical properties of the 6061 Al alloys after a single pressing by ECAP, Scripta Mater. 53 ,2005, pp. 1207-1211. [11] W.J. Kim, J.K. Kim, T.J. Park, S.I. Hong, D.I. Kim, Y.S. Kim and J.D. Lee, Enhancement of strength and superplasticity in a 6061 Al alloy processed by equal-channel-angular-pressing, Metall. Mater. Trans. A33 2002, pp. 3155-3164. [12] S. Ferrasse, V.M. Segal, K.T. Hartwig and R.E. Goforth, Development of a submicrometer-grained microstructure in aluminum 6061 using ECAE, J. Mater. Res. 5,1997, pp. 1253-1261. [13] E.A. El-Danaf, M.S. Soliman, A.A. Almajid, and M.M. El-Rayes, Enhancement of mechanical properties and grain size refinement of commercial purity aluminum 1050 processed by ECAP, Materials Science and Engineering A 458 ,2007, pp. 226-234. [14] Ruslan Z. Valiev, and Terence G. Langdon, Principles of equal-channel angular pressing as a processing tool for grain refinement, Progress in Materials Science 51, 2006 pp. 881-981. [15] Terence G. Langdon, The principles of grain refinement in equalchannel angular pressing, Materials Science and Engineering A 462, 2007, pp. 3-11. [16] T. kovářík , J. Zrník , M. Cieslar, Mechanical Properties and Microstructure Evolution in ECAP Processed Al-Mg-Si Alloy, Rožnov pod Radhoštěm , 2010, pp. 1-6. [17] G. Angella, B.E. Jahromi, M.Vedani, A comparison between equal channel angular pressing and asymmetric rolling of silver in the severe plastic deformation regime, Materials Science & Engineering A 559, 2013, pp. 742-750. [18] C. Mallikarjuna, S.M. Shashidhara, U.S. Mallik, Evaluation of grain refinement and variation in mechanical properties of ECA pressed 2014 aluminum alloy, Mat. and Design 30, 2009, pp. 1638-1642 [19] J. Jiang, Y.Wang , J. Qu, Microstructure and mechanical properties of AZ61 alloys with large cross-sectional size fabricated by multi-pass ECAP, Mat. Science & Engineering A 560, 2013, pp. 473-480. [20] I. Mazurina, T. Sakai, H. Miura, O. Sitdikov, and R. Kaibyshev, Grain refinement in aluminum alloy 2219 during ECAP at 250 ◦C, Materials Science and Engineering A 473, 2008, pp. 297-305. [21] C. Xu, M. Furukawa, Z. Horita, Terence G. Langdon, The evolution of homogeneity and grain refinement during equal-channel angular pressing: A model for grain refinement in ECAP, Materials Science and Engineering A 398, 2005, pp. 66-76. [22] H.G. Salem, and A.A. Sadek," Fabrication of High Performance PM Nanocrystalline Bulk AA2124", Journal of Materials Engineering and Performance,2009, pp. 356-367. [23] R.Z. Valiev, H.J. Rovan, M. Liu, M. Murashkin, A.R. Kilmametov, T. Ungar, and L. Balogh," Nanostructures and Microhardness in Al and Al– Mg Alloys Subjected to SPD", Materials Science Forum, Vols. 604-605, 2009, pp. 179-185. [24] F. Wetscher, A. Vorhauer, and R. Pippan, "Strain hardening during high pressure torsion deformation", Material Science and Engineering, A410- 411, 2005, pp. 213-216. [25] D.J. Chakrabarti, D.E. Laughlin, "Phase relation and precipitation in Al- Mg-Si alloys with Cu additions", Progress in Materials Science, Vol. 49, 2004, pp. 389-410. [26] J. Zhang, N. Gao, M. J. Starink, "Al–Mg–Cu based alloys and pure Al processed by high pressure torsion: The influence of alloying additions on strengthening", Materials Science and Engineering, A 527, 2010, pp. 3472–3479.