Spark Plasma Sintering of Aluminum-Based Composites Reinforced by Nanocrystalline Carbon-Coated Intermetallic Particles

Creators

Description

Aluminum Matrix Composites reinforced with
nanocrystalline Ni3Al carbon-coated intermetallic particles, were
synthesized by powder metallurgy. Powder mixture of aluminum
with 0.5-volume fraction of reinforcement particles was compacted
by spark plasma sintering (SPS) technique and the compared with
conventional sintering process. The better results for SPS technique
were obtained in 520ºC-5kN-3min.The hardness (70.5±8 HV) and the
elastic modulus (95 GPa) were evaluated in function of sintering
conditions for SPS technique; it was found that the incorporation of
these kind of reinforcement particles in aluminum matrix improve its
mechanical properties. The densities were about 94% and 97% of the
theoretical density. The carbon coating avoided the interfacial
reaction between matrix-particle at high temperature (520°C) without
show composition change either intermetallic dissolution.

Files

9998350.pdf

Files (4.2 MB)

Name Size Download all
md5:7ddb9f3a1cb140a01cc38b3b1594ba54
4.2 MB Preview Download

Additional details

References

  • M. Rahimian, N. Ehsani, N. Parvin, H.R. Baharvandi, The effect of particle size, sintering temperature and sintering time on the properties of Al–Al2O3 composites, made by powder metallurgy, J. Mater. Process. Tech., 209, 2009,pp. 5387–5393.
  • K. Wieczorek, Gamrat, NiAl/Ni3Al-Al2O3 composite formation by reactive ball milling, J. Therm. Anal. Cal., 82, 2005, pp. 719-724.
  • M.H. Enayati, Z. Sadeghian, M. Salei, A. Saidi, The effect of milling parameters on the synthesis of Ni3Al intermetallic compound by mechanical alloying, Mater. Sci. and Eng. A, 2004, pp. 809-81.
  • J. B. Fogagnolo, F. Velasco, M. H. Robert, J. M. Torralba, Effect of mechanical alloying on the morphology, microstructure of aluminum matrix composite powders, Mater. Sci. and Eng. A, 342, 2003, pp. 131- 143.
  • R.A. Varin, Structural and Functional Intermetallics- an Overview, Eng. Materials, 5 (2001) R. XXII, 1, 1996, pp. 11-18.
  • P. Matteazzi, G. Le Caer, J. Am. Ceram. Soc., 75, 1992, num.10, pp. 2749-2755.
  • T.F. Grigorera, A.P. Barinova, N.Z. Lyaknhov, Russian Chem. Rev., 70, 2001.
  • D. Oleszak, J. Mater. Sci., 39, 2004, pp. 5169-5174.
  • C.T. Liu, D.P. Pope, Ni3Al and its Alloys, J.H. Westbrook, R.L. Fleischer Eds., Intermetallic Compounds, 2, 2000, Wiley, New York, pp. 17-47. [10] C. Suryanarayana, Mechanical Alloying, Prog. Materials Science, 46, 2001. [11] S. Boucetta, T. Chihi, B. Ghebouli, M. Fatmi, First-principles study of the elastic and mechanical properties of Ni3Al under high pressure, Mater. Sci-Poland-1,28,2010. [12] M. Lieblich, J.L Gónzalez, G. Caruana, Thermal Stability of an Al/Ni3Al Composite Processed by Powder Metallurgy, Intermetallics, 5, 1997,pp. 515-524. [13] R.G. Esquivel, E.M. Orozco, C.T. Renero, D.V. Jaramillo, Dynamic compaction domain (shock compaction energy vsρ0/ρ) for a Fe-15 atromic % Cu nanometric alloy obtained by mechanical alloying, J. Phys. IV France, 110, 2003, pp. 803-808. [14] Powder diffraction file JCPDF (2006) 03-065-0430, (a=0.15406 nm, Cu kα1).