STUDY OF THE MECHANICAL DURABILITY OF A HIGH-PRESSURE POLYETHYLENE FILM AND ITS COMPOSITION AT VARIOUS TEMPERATURES

Abstract

In addition, it was found that, in contrast to the original LDPE, when an additive of the optimal amount (LDPE + 0.05 wt.% phthalic anhydride + 0.05 wt.% orthophenylenediamine) is introduced into the composition of LDPE, it leads to a noticeable increase in mechanical durability. The mechanical durability of LDPE and its modifications at different temperatures was studied, and an increase in its durability took place due to the combined effect of external physical factors. It has been established that the activation energy in both cases is constant and does not depend on the introduction of additives into LDPE. The increase in the mechanical strength of the LDPE modification can be explained by the structure-forming features of the FA and OPD additives, which contribute to the close packing of macromolecules during the formation of polymeric materials.

Аннотация

Кроме того, установлено, что в отличие от исходного ПЭВД, при введении в состав ПЭВД добавки оптимального количества (ПЭВД+0,05масс.% фталевый ангидрид+0,05масс.% ортофенилендиамин ) приводит к заметному увеличению механической долговечности. Была исследовано механическая долговечность ПЭВД и его модификации при различных температурах и имело место повышение его стойкости комплесным воздействием внешних физических факторов. Установлено, что энергия активации в обоих случая постоянен и не зависит от введения добавок в ПЭВД. Увеличение механической прочности модификации ПЭВД можно обьяснить структурообразующими особенностями добавки ФА и ОФД, которые способствуют плотной упоковке макромолекул при формировании полимерных материалов.