Development of Low-Carbon Autoclaved Aerated Concrete Using an Alkali-Activated Ground Granulated Blast Furnace Slag and Calcium Carbide Slag

The environmental impact of traditional construction materials has led to increasing interest in developing more sustainable alternatives. This study addresses the development of low-carbon autoclaved aerated concrete (AAC) through the complete replacement of ordinary Portland cement (OPC) with ground granulated blast furnace slag (BFS), activated with lime and, in some formulations, supplemented with calcium carbide slag (CCS). Five different AAC mixtures were prepared and evaluated in terms of workability, foaming behavior, compressive strength, phase composition, density, thermal conductivity, and life cycle assessment (LCA). The BFS-based mixtures activated with lime exhibited good workability and foaming stability. After pre-curing, the addition of CCS significantly improved the formation of tobermorite during autoclaving. As a result, the BFS–CCS formulations achieved compressive strengths comparable to the reference OPC-based mix while maintaining low densities (420–441 kg/m³) and thermal conductivities in the range of 0.111–0.119 W/(m·K). These results confirm the technical feasibility of producing structural-grade AAC with a lower environmental footprint.