Abstract
The phase equilibrium in the PbSe-Mn system was studied by the methods of physicochemical analysis (DTA, XRD, MCA, as well as measurements of density and microhardness) and its T-x phase diagram was constructed. It has been established that the PbSe-Mn system is a non-quasi-binary region of the Pb-Mn-Se ternary system. Single-phase alloys crystallize below the solidus line in the PbSe-Mn system at a concentration of 0-5 at. % Mn. In the concentration range of 5–10 at. % Mn, there is a two-phase region consisting of α+PbMnSe2(S). In other areas of the system below the solidus line, there are three-phase areas. Three-phase alloys consisting of (α+S+Pb) crystallize in the region of 10-22 at. % Mn. In the area of concentration 22-30 at. % Mn, there is a three-phase region consisting of (Pb+MnSe+S). Three-phase alloys consisting of (MnSe+Pb+Mn) crystallize in the range of 35-100 at. % Mn.
Аннотация
Методами физико-химического анализа (ДТА, РФА, МCА, а также измерением плотности и микротвердости) изучено фазовое равновесие в системе PbSe-Mn и построена ее Т-х фазовая диаграмма. Установлено, что система PbSe-Mn является неквазибинарным сечением тройной системы Pb-Mn-Se. Однофазные сплавы кристаллизуются ниже линии солидуса в системе PbSe-Mn при концентрации 0-5 ат. % Mn. В области концентрации 5–10 ат. % Mn имеется двухфазная область, состоящая из α+PbMnSe2(S). В остальных областях системы ниже линии солидуса имеются трехфазные области. Трехфазные сплавы, состоящие из (α+S+Pb), кристаллизуются в области 10-22 ат. % Mn. В области концентрации 22-30 ат. % Mn имеется трехфазная область, состоящая из (Pb+MnSe+S). Трехфазные сплавы, состоящие из (MnSe+Pb+Mn), кристаллизуются в интервале 35-100 ат. % Mn.
Notes
Список литературы:
1. 1. Norihiro Suzuki, Katsuyuki Sawai, and Sadao Adachi. Optical properties of PbSe// Journal of Applied Physics. 1995. V.77. P. 1249. https://doi.org/10.1063/1.358926
2. Ribeiro, G. A. S. et al. Strong anharmonicity in the phonon spectra of PbTe and SnTe from first principles // Phys. Rev. 2018. B 97. P. 014306.
3. 3. Delaire O. et al. Giant a harmonic phonon scattering in PbTe // Nat. Mater. 2011. V. 10. P. 614-618.
4. Chen Y., Xinyuan A. & Marianetti C. A. First-principles approach to nonlinear lattice dy-namics: anomalous spectra in PbTe // Phys. Rev. Lett. 2014. V. 113. P. 105501.
5. Gayner C., Kar K. K. & Kim W. Recent progress and futuristic developments of PbSe thermoelectric materials and devices // Mater. Today Energy. 2018. V. 9. P. 359–376.
6. Shulumba N., Hellman O. & Minnich A. J. Intrinsic localized mode and low thermal con-ductivity of PbSe // Phys. Rev. 2017. V. 95. P. 014302.
7. Chen Z. et al. Vacancy-induced dislocations within grains for high-performance PbSe thermoelectrics // Nat. Commun. 2017. V. 8. P. 13828.
8. Romero A. H. Gross, E. K. U., Verstraete, M. J. & Hellman, O. Thermal conductivity in PbTe from first principles // Phys. Rev. 2015. V. 91. P. 214310.
9. Wang H., Pei Y., LaLonde A. D. & Snyder, G. J. Weak electron–phonon coupling con-tributing to high thermoelectric performance in n-type PbSe // Proc. Natl Acad. Sci. USA 2012. 109. P. 9705–9709.
10. Ribeiro, G. A. S. et al. Strong anharmonicity in the phonon spectra of PbTe and SnTe from first principles // Phys. Rev. 2018 V. 97. P. 014306.
11. Ribeiro G. A. S. et al. Strong anharmonicity in the phonon spectra of PbTe and SnTe from first principles // Phys. Rev. 2018. B 97. S.014306.
12. Li, C. W. et al. Phonon self-energy and origin of anomalous neutron scattering spectra in SnTe and PbTe thermoelectrics // Phys. Rev. Lett. 2014. V. 112. P. 175501.
13. Янушкевич К.И., Викторов И.А., Боднарь И.В. Кристаллическая струк-тура и магнитная восприимчивость CuInSe2)ı.x(2MnSe)x. // Ж. Физи¬ка твердого тела, 2009. 51. № 1. C. 104-108.
14. Маковецкий Г.И., Галяс А.И., Янушкевич К.И. Структурные, магнитные и элек-трические свойства твердых растворов системы теллурид хрома- теллурид марганца // ФТТ. 1997. Т.39. № 2. С. 320-324.
15. Маковецкий Г.И., Галяс А.И. Нейтронографическое исследование структурных и магнитных фазовых переходов в селениде марганца // Физика твердого тела. 1982. Т.24. № 9, С. 2753 2756.
16. Mullin D.P., Galazka R.R., Furdyna J.K. Microwave helicon propagation and the dy-namic magnetic susceptibility in Hgi.xMnxSe // Phys. Rev. 1981. V.24. № 1. P. 355-362
17. Аплеснин С.С., Рябинкина Л.И., Романова О.Б., Бадаев Д.А., Демиденко О.Ф., Янушкевич К.И., Мирошниченко Н.С. Влияние орбитального упорядочения на транспорт-ные и магнитные свойства MnSe и МпТе // ФТТ. 2007. Т.49. № 11. С.1984-1989.
18. 18. Bodnar I.V. Optical properties of CuInSe2)i-x (2MnSe)x alloys. // Semicon¬ductors, 2010. 44. № 5. P. 581-584.
19. Рустамов П.Г., Сафаров М.Г., Алиев И.И., Ильясов Т.М. Исследование химиче-ского взаимодействия в системе As2Se3–MnSe // Журн. неорган. химии. 1978. T. 23. № 1. C. 151-155.
20. Аллазова Н.М., Ильясли Т.М. Фазовое равновесие в системе CuInSe2 - Pb // Вест-ник Бакинского университета, сер. ест. наук. 2008. № 4. С. 37-41.
21. Аллазова H.M. Фазовая диаграмма системы CuInSe2-PbSe // Вестник Ба-кинского Университета, сер.ест.наук. 2006. № 2. C.23-27.
22. Алиев И.И., Ильяслы Т.М., Гасангулиева Ш.А., Велиев Дж.А. Фазовые равнове-сия и стеклообразование в системе AsSe-MnSe // Неорган.материалы. 2011. T.47. № 7. C.784-787.
23. Заргарова М.И., Мамедов А.Н., Аждарова Дж.С., Ахмедова (Велиев) Дж.А., Аби-лов Ч.И. Справочник: Неорганические вещества, синтезированные и исследованные в Азер-байджане. Баку. Изд. Элм. 2004. 462 c.
24. Физико-химические свойства полупроводниковых веществ. Справочник. М.: Наука. 1979. 399 c.
25. Диаграммы состояния двойных металлических систем. Справочник: В 3т: Т.3 // Под. Ред. Н.П. Лякишева. М.: Машиностроение. 1997. 1023 c.