Stress, Strain, and Temperature measurement data for AISI 301 and AISI 316 stainless steels from tension tests with a sudden increase of strain rate
Authors/Creators
- 1. IMPACT – Multiscale Mechanics Research Group, Engineering Materials Science, Faculty of Engineering and Natural Sciences (ENS), Tampere University, POB 589, 33014 Tampere, Finland
Description
This publication comprise data obtained during a tension test where the strain rate was suddenly changed from 10-4 s-1 to 1.3x103 s-1. The sudden increase in strain rate was carried out at different amounts of plastic strain. The tests were carried out with a modified tension Split-Hopkinson Pressure bar device. The force was measured from the stress bars using strain gages, whereas the strain was measured using high speed photography and digital image correlation. The temperature was measured using high speed infrared imaging. The data is part of the original publication in Journal of Dynamic Behavior of Materials. The original manuscript is available at https://doi.org/10.1007/s40870-022-00333-y
Files
Files
(1.6 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:b8db189609c3cae256904b8370d068e2
|
1.5 MB | Download |
|
md5:e73c7a3398261a05d7ddbaa2f329931b
|
44.0 kB | Download |
|
md5:5a25581da58a1498aab6003eb82f1657
|
44.7 kB | Download |
Additional details
Related works
- Is documented by
- Journal article: 10.1007/s40870-022-00333-y (DOI)
Funding
- Research Council of Finland
- Dynamics of the Microplasticity of Metastable Austenite in Steels 294845