Dataset of "Preparation of novel lithiated high-entropy spinel type oxyhalides and their electrochemical performance in Li-ion batteries "

Electrochemical measurements carried out using the 2032-coin cells with the Li-metal anode have shown voltammetric charge capacities of 450, 694, and 593 mAh g-1 for HEOFe, LiHEOFeCl, and LiHEOFeF, respectively.
Galvanostatic chronopotentiometry at 1 C rate confirmed high initial charge capacities for all the samples but galvanostatic curves exhibited a capacity decay over 100 charging/discharging cycles. Raman spectroelectrochemistry measured on the LiHEOFeF sample proved the reversibility of the electrochemical process for initial charging/discharging cycles. Electrochemical impedance spectroscopy revealed the lowest initial charge transfer resistance for LiHEOFeCl and its gradual decrease both for LiHEOFeCl and LiHEOFeF during galvanostatic cycling, whereas the charge transfer resistance of HEOFe slightly increases over 100 galvanostatic cycles due to different mechanism of the electrochemical reduction.