Microscopic mechanism of the L1_2–D0_19 phase transformation in a Co-base single crystal superalloy

This record contains datasets related to the publication:

N. Karpstein et al., Microscopic mechanism of the L1₂-D0₁₉ phase transformation in a Co-base single crystal superalloy, Acta Materialia (2024), doi:10.1016/j.actamat.2024.120416.

A readme file containing descriptions of datatypes can be found in the main folder.

Abstract:

In γ′-strengthened superalloys based on the Co-Al-W system, the stability of the γ′ phase is often limited, as it is found to transform into other phases such as B2 and D0₁₉ after long-term annealing. To explore the details behind the annealing-induced transformation from the metastable L1₂-γ′ phase to the thermodynamically stable D0₁₉-χ phase in the single-crystalline Co-base superalloy ERBOCo-VF60 (Co_79.8Al_8.9W_9.0Ta_2.3 in at.%), scanning transmission electron microscopy and atom probe tomography are employed. Due to the structural similarity between the L1₂ and D0₁₉ structures, coherent plate-shaped χ precipitates are formed in the γ/γ′ microstructure parallel to {111} planes through a shear-based transformation mechanism. While the χ phase precipitates slowly during isothermal aging, its formation can be significantly accelerated locally by coating the superalloy with a Cr-rich layer, which indirectly stabilizes the χ phase as revealed by thermodynamic calculations. This procedure allowed us to obtain an intermediate (incomplete) state of χ-phase formation in terms of both crystal structure and composition. By characterizing the partial dislocations at the tip of growing χ precipitates, the microscopic details of the shear-based cubic-to-hexagonal transformation from L1₂ to D0₁₉ are uncovered. The compositional aspect of the transformation involves a significant diffusion-mediated enrichment of W in the χ phase, accompanied by a simultaneous W depletion in the γ′ phase, leading to its transformation to the γ phase.