Literature |
Cycled Areal Cap. (mAh/cm2) |
Discharge Energy (Wh/kg) |
Discharge Power (W/kg) |
Disc. Current Density (mA/cm2) |
Energy Efficiency |
Comments |
|
|
|
|
|
Chang 17 ACS-AMI |
30 |
133 |
72.3 |
10 |
95 |
150 cycles 1g, 3cm2, 190C |
|
|
|
|
Chang 18 |
65 |
405 |
75.6 |
10 |
93.8 |
300 cycles Data for
Ni/NaCl=1.25 1g 3cm2 190C, no SOC limitation |
Chang 17 JPS |
30 |
219.6 |
73.2 |
10 |
94.3 |
157 mAh=100SOC |
|
|
|
|
|
Li 14 JPS-Improved |
30 |
215.1 |
71.7 |
10 |
88.7 |
|
|
|
|
|
|
|
Jung 18 |
47.6 |
355 |
65.25 |
10 |
95 |
no SOC limitation
143mAh/g |
|
|
|
|
Li 16 |
45.7 |
340 |
25 |
10 |
91.6 |
190C 25 mW cm-2 no SOC
lim largest SOC window |
|
|
|
43.4 |
300 |
75 |
30 |
86.5 |
190C 75 mW cm-2 no SOC
lim largest SOC window |
|
|
|
45 |
258 |
25 |
10 |
92.3 |
280C 25 mW cm-2 no SOC
lim largest SOC window |
|
|
|
41.8 |
220 |
75 |
30 |
88.4 |
280C 75 mW cm-2 no SOC
lim largest SOC window |
|
|
Lu 17 |
125.4 |
295 |
75 |
31.5 |
86 |
|
|
|
|
|
|
|
|
117.6 |
279 |
100 |
42 |
84.8 |
|
|
|
|
|
|
|
Present Work |
135 |
355.1575 |
13.15398 |
5 |
96.73854 |
|
|
|
|
|
|
|
|
135 |
352.3239 |
26.09807 |
10 |
95.27704 |
|
|
|
|
|
|
|
|
135 |
349.8127 |
38.86807 |
15 |
93.79984 |
|
|
|
|
|
|
|
|
135 |
346.1639 |
51.28355 |
20 |
92.40258 |
|
|
|
|
|
|
|
|
135 |
339.5072 |
75.44604 |
30 |
90.57585 |
|
|
|
|
|
|
|
|
135 |
332.6939 |
98.57597 |
40 |
88.8063 |
|
|
|
|
|
|
|
|
135 |
325.9802 |
120.7334 |
50 |
86.85502 |
|
|
|
|
|
|
|
|
135 |
303.7864 |
180.0216 |
80 |
80.95777 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Gustav 21 |
40 |
321 |
|
20 |
96.10778 |
2.560305 |
20 |
|
|
|
|
|
|
40 |
318 |
|
30 |
95.20958 |
2.520147 |
20 |
|
|
|
|
|
|
40 |
313 |
|
50 |
93.71257 |
2.359756 |
20 |
|
|
|
|
|
|
40 |
303 |
|
80 |
90.71856 |
2.439902 |
20 |
|
|
|
|
|
|
40 |
298 |
|
100 |
89.22156 |
2.359756 |
20 |
|
|
|
|
|
|
40 |
292 |
|
120 |
87.42515 |
2.359756 |
20 |
|
|
|
|
|
|
40 |
286 |
|
140 |
85.62874 |
2.359756 |
20 |
|
|
|
|
|
|
40 |
282 |
|
160 |
84.43114 |
2.270819 |
20 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|