Synthesis of Vic-Dioxime Palladium (II) Complex: Precursor for Deposition on SBA-15 in ScCO2
Description
Synthesizing supercritical carbon dioxide (scCO2) soluble precursors would be helpful for many processes of material syntheses based on scCO2. Ligand (amphi-(1Z, 2Z)-N-(2-fluoro-3-(trifluoromethyl) phenyl)-N'-hydroxy-2-(hydroxyimino) were synthesized from chloro glyoxime and flourus aniline and Pd(II) complex (precursor) prepared. For scCO2 deposition method, organometallic precursor was dissolved in scCO2 and impregnated onto the SBA-15 at 90 °C and 3000 psi. Then the organometallic precursor was reduced with H2 in the CO2 mixture (150 psi H2 + 2850 psi CO2). Pd deposited support material was characterized by ICP-OES, XRD, FE-SEM, TEM and EDX analyses. The Pd loading of the prepared catalyst, measured by ICP-OES showed a value of about 1.64% mol/g Pd of catalyst. Average particle size was found 5.3 nm. The catalytic activity of prepared catalyst was investigated over Suzuki-Miyaura C-C coupling reaction in different solvent with K2CO3 at 50 oC. The conversion ratio was determined by gas chromatography.
Files
10005810.pdf
Files
(1.2 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:df1821b88265fa9340e944a5b9e14148
|
1.2 MB | Preview Download |
Additional details
References
- Y. Zhang, C. Erkey, "Preparation of supported metallic nanoparticles using supercritical fluids: a review," J. Supercrit. Fluids, vol. 38, pp. 252, 2006.
- C. Erkey, "Preparation of metallic supported nanoparticles and films using supercritical fluid deposition," J. Supercrit. Fluids, vol. 47, pp. 517, 2009.
- X.R. Ye, Y. Lin, C.M. Wai, "Decorating catalytic palladium nanoparticles on carbon nanotubes in supercritical cabon dioxide," Chem. Commun., vol. 5, pp. 642, 2003.
- S.E. Bozbag, C. Erkey, "Supercritical deposition: Current status and perspectives for the preparation of supported metal nanostructures" J. Supercrit. Fluids, vol. 96, pp. 298, 2015.
- Lin, Chi-Kai, "Novel synthesis and characterization of precious-metal nanocatalysts for clean energy applications," N. IL. Uni., pp. 128, 2011.
- S.K. Morley, P.C. Marr, P.B. Webb, A.R. Berry, F.J. Allison, G. Moldovan, P.D. Brown, S.M. Howdle, "Clean preparation of nanoparticulate metals in porous supports: a supercritical route," J. Mater. Chem., vol. 12, pp. 1898, 2002.
- A. Bayrakceken, U. Kitkamthorn, M. Aindow and C. Erkey, "Decoration of multi-wall carbon nanotubes with platinum nanoparticles using supercritical deposition with thermodynamic control of metal loading" Scripta Materialia, 56, 101–103, 2007
- J. Baoa, H. Tianb, R. Tang, "Synthesis and characterization a novel europium(III)-β-diketonate complex with carbazole and triphenylamine moieties" Inorganica Chimica Acta, vol.401, pp.19–23, 2013.
- A.L. Dantas, P.D. Alves, D. Arando, M. Schmal, "Characterization of carbon supported Pd catalysts: Influence of electronic and particle size effects using reaction probes" Appl. Catal., vol 277, pp. 71-81, 2004. [10] Hunt A. J., Budarin V. L., Comerford J. W., Parker H. L., Lazarov V. K., Breeden S.W., Macquarrie D. J., Clark J. H.. "Deposition of Palladium Nanoparticles in SBA-15 Templated Silica Using Supercritical Carbon Dioxide" Materials Letters vol.116, pp. 408–411, 2014. [11] Cotugno, P., M. Casiello, A. Nacci, P. Mastrorilli, M. M. Dell'Anna and A.Monopoli. "Suzuki coupling of iodo and bromoarenes catalyzed by chitosan-supported Pd-nanoparticles in ionic liquids" Journal of Organometallic Chemistry vol. 752: pp.1-5, 2014.