Deposition Rate and Energy Enhancements of TiN Thin-Film in a Magnetized Sheet Plasma Source
Creators
Description
Titanium nitride (TiN) has been synthesized using the sheet plasma negative ion source (SPNIS). The parameters used for its effective synthesis has been determined from previous experiments and studies. In this study, further enhancement of the deposition rate of TiN synthesis and advancement of the SPNIS operation is presented. This is primarily achieved by the addition of Sm-Co permanent magnets and a modification of the configuration in the TiN deposition process. The magnetic enhancement is aimed at optimizing the sputtering rate and the sputtering yield of the process. The Sm-Co permanent magnets are placed below the Ti target for better sputtering by argon. The Ti target is biased from –250V to – 350V and is sputtered by Ar plasma produced at discharge current of 2.5–4A and discharge potential of 60–90V. Steel substrates of dimensions 20x20x0.5mm3 were prepared with N2:Ar volumetric ratios of 1:3, 1:5 and 1:10. Ocular inspection of samples exhibit bright gold color associated with TiN. XRD characterization confirmed the effective TiN synthesis as all samples exhibit the (200) and (311) peaks of TiN and the non-stoichiometric Ti2N (220) facet. Cross-sectional SEM results showed increase in the TiN deposition rate of up to 0.35μm/min. This doubles what was previously obtained [1]. Scanning electron micrograph results give a comparative morphological picture of the samples. Vickers hardness results gave the largest hardness value of 21.094GPa.
Files
5984.pdf
Files
(251.1 kB)
| Name | Size | Download all |
|---|---|---|
|
md5:aa64427495c7102b242849e93f73bbe6
|
251.1 kB | Preview Download |
Additional details
References
- V. R. Noguera and H. J. Ramos, "A magnetized sheet plasma source for the synthesis of TiN on stainless steel substrates." Thin Solid Films 613, 2006, pp. 506-507.
- M. Guemmaz, A. Masser, and J. Grob, "Ion implantation processing of sub-stoichiometric titanium nitrides and carbonitrides: chemical structural andmicromechanical investigations." Applied Physics A 64, 1997, pp. 407-415.
- R. Bahl, A. Kumar, M. Vedawyas, and D. Patel, "Synthesis and characterization of TiC and TiCN coatings." Applied Physics A [Suppl.], 1999, S643-S646.
- H. Ramos, and R. Awayan, R. "Nitride formation using a magnetized sheet plasma source." Vacuum 65, 2002, 397-402.
- S. Fortuna, Y. Sharkeev, A. Perry, J. Matossian, and I. Shulepov,"Microstructural features of wear resistant titanium nitride coatings deposited by different methods." Thin Solid Films 377-378, 2000, 512-517.
- J.H. Hsieh, and C. Li, "Calculation of sputtering rate by a Monte Carlomethod." Journal of Materials Science Letters 22, 2003, 1125- 1126.
- N. Matsunami, Y. Yamamura, Y. Itikawa, N. Itoh, Y. Kazumata, S. Miyagawa, K. Morita, and R. Shimizu, "Energy dependence of sputtering yields of monoatomic solids." Institute of Plasma Physics Journal -AM 14, 1980, 1-15.