 Pattern#  1 Phase No.:   1 Phase name: The Preparation of eta Alumina
 --------------------------------------------------------------------------------------------------------------

   No.  Code     H   K   L  Mult      Hw      ETA/M    2theta/TOF     Icalc       Iobs      Sigma     StrFactor^2    d-hkl       CORR

      1   1      1   1   1     8  0.701779  0.000010       6.207      179.0      238.2      0.088       1731.4170  4.554754      0.954540
      2   1      2   2   0    12  0.701964  0.000010      10.145        1.4      199.3      0.061         26.5862  2.789206      0.883319
      3   1      3   1   1    24  0.702075  0.000010      11.901      184.7      316.8      0.057       2464.4656  2.378643      0.843163
      4   1      2   2   2     8  0.702113  0.000010      12.433       79.9      123.0      0.037       3544.8215  2.277377      0.830188
      5   1      4   0   0     6  0.702263  0.000010      14.365      333.8      294.5      0.055      27951.0566  1.972266      0.780252
      6   1      3   3   1    24  0.702376  0.000010      15.662       47.6       26.3      0.036       1237.8256  1.809876      0.744782
      7   1      4   2   2    24  0.702566  0.000010      17.617        9.9       76.6      0.032        349.7529  1.610349      0.689212
      8   1      3   3   3     8  0.702682  0.000010      18.695        0.0        0.0      0.000          0.0111  1.518251      0.657880
      9   1      5   1   1    24  0.702682  0.000010      18.695       94.5      194.6      0.040       3944.0715  1.518252      0.657880
     10   1      4   4   0    12  0.702875  0.000010      20.370      433.3      594.5      0.056      46219.4648  1.394603      0.608794
     11   1      5   3   1    48  0.702992  0.000010      21.314       52.7       39.0      0.026       1608.7678  1.333496      0.581118
     12   1      4   4   2    24  0.703031  0.000010      21.620        1.6        3.0      0.003        104.9968  1.314844      0.572175
     13   1      6   2   0    24  0.703188  0.000010      22.804        3.8       30.5      0.021        285.1931  1.247371      0.537759